0.5mm 0.8mm 52H Glass Sealing Vacodil 520 Resistance Wire

52H Glass Sealing52 Vacodil 520 Wire 0.5mm and 0.8mm large in stock with fast delivery

Heat Treatment For Alloy52
(1) Stress relief annealing In order to eliminate the residual stress of parts after machining, stress relief annealing is required: 430~540℃, heat preservation 1~2h, furnace cooling or air cooling. [1]
(2) Intermediate annealing In order to eliminate the work hardening phenomenon caused by the alloy in the process of cold rolling, cold drawing and cold stamping, in order to facilitate the continued processing. The workpiece needs to be heated to 700~800℃ in a vacuum or protective atmosphere for 30~60min, then furnace cooled, air cooled or water quenched.
(3) Pre-oxidation treatment When the combined gold is used as a sealing material, it should be pre-oxidized before sealing. A uniform and dense oxide film is formed on the surface of the alloy. The parts are heated in saturated wet hydrogen at 1100°C for 30 minutes, and then oxidized in the air at about 800°C for 5-10 minutes. The weight gain of the parts should be 0.1~0.3mg/cm2

Vacodil 520 Resistance Wire

0.8mm Resistance Wire

FeNi52 Resistance Wire

0.5mm 0.8mm 52H Glass Sealing Vacodil 520 Resistance Wire Images